No.;Material name;Regulatory document which regulates the material delivery to the plant;Basic material requirements

1;Copper wire;Technical Specifications (TU) 16-705.492-2005;Wire brand — MM or MT, wire diameter — 1.76 mm. The wire should stretch to a minimum diameter of 0.40 mm. Electrical resistivity: for MM brand — 0.01724 Ohm · m · 10-6. For MT brand — 0.01780 Ohm · m · 10-6. 2;Copper tinned wire;GOST R (State Standard R) 53803-2010 Technical Specifications (TU) 16-505.850-75;Rod brand — M001 or M001b. Rod diameter — 8.0 mm. Electrical resistivity — 0.01707 Ohm · m · 10-6. Wire diameter — 0.40 mm 3;Low carbon steel wire for general use, galvanized steel wire;GOST (State Standard) 3282-74;Type of wire processing — heat treated (HT), untreated (UT). Wire diameter — 0.9-1.2 mm The wire must have a galvanized coating. A method of galvanization — hot dip galvanizing Rupture strength for HT — 340-540 N/mm?. For UN — 690-1180 N/mm?. Coil size dimension for UN: inner diameter — 355 mm, outer diameter — 650 mm max, height — 300 max 4;Steel rope wire;GOST (State Standard) 7372-79;Wire diameter — 0.90-1.00 mm The wire must have a galvanized coating. A method of galvanization — hot dip galvanizing Rupture strength — 1570-1670 N/mm?. Coil size dimension for UN: inner diameter — 355 mm, outer diameter — 650 mm max, height — 300 max 5;Alum-polyethylene tape;Technical Specifications (TU) 7417-001-0032300-2006;Tape thickness — 0.135 mm, aluminum layer thickness — 0.100 mm, tape width — 15-135 mm in increments of 5 mm. Inner bushing diameter — 76 mm 6;Foil composite flexible alumoflex material;Technical Specifications (TU) 2358-017-50157149-2004;Tape thickness — 0.070 mm, aluminum layer thickness — 50 mm (other tape thicknesses is also possible). Tape width — 20-50 mm in increments of 5 mm 4 inner bushing diameter — 76 mm 7;Polyethylene terephthalate film PEF-E;GOST (State Standard) 24234-80;Film thickness — 0.020-0.035 mm. Tape width — 12, 15-130 mm in increments of 5 mm. Cutting film width — 600 mm. Coil inner diameter — 76 mm 8;Fiberglass bar;Technical Specifications (TU) 2296-001-98155183-07;Bar diameter — 0.8-2.4 mm Fiberglass rods should come on the drums: drum type — up to 10. Width between drum flange — 620 mm 9;Hydrophobic filler for telephone cable filling;Technical Specifications (TU) 0254-001-31999055-2002;The filler should be compatible with insulation polyethylene. Storage container — barrels with a diameter of 570 mm 10;Acrylic coloring for optic fiber;Data sheets and quality certificates of manufacturers; 11;Polyethylene compositions for insulation 102-02K, 107-02K;GOST (State Standard) 16336-77; High pressure polyethylene of low density. ?= 0.920-0.925 g/cm?. Melt flow rate — 0.24-0.36 g/10 min 12;Imported polyethylene for copper core insulation;Data sheets and quality certificates of manufacturers; High pressure polyethylene of low density. ?= 0.920-0.925 g/cm?. Melt flow rate — 0.24-0.36 g/10 min 13;Polyethylene composition for sheaths 102-10K. 153-10K;GOST (State Standard) 16336-77 ;High pressure polyethylene of low density. ?= 0.935-0.950 g/cm?. Melt flow rate — 0.21-0.39 g/10 min 14;Imported polyethylene for cable sheathing;Data sheets and quality certificates of manufacturers;High, medium and low pressure polyethylene designed for cable sheathing 15;Polyethylene composition for cable sheath 107-61K;GOST (State Standard) 16336-77 ;High pressure polyethylene of low density. ?= 0.960-0.980 g/cm?. Melt flow rate — 2.0-3.0 g/10 min Flammability — fades when removed from the flame 16;PPG1035-08 polypropylene;Technical Specifications (TU) 2211-008-50236110-2006;Melt flow rate — 3.0-4.0 g/10 min, polypropylene for mixing with polyethylene 17;Polyvinyl chloride insulation plastic compound type I40-13A;GOST (State Standard) 5960-72; 18;Polyvinyl chloride cable-sheathing plastic compound types О-40, ОМ-40;GOST (State Standard) 5960-72; 19;Polyvinyl chloride plastic compound of low fire hazard types PPO 30-35, PPI 30-30;Technical Specifications (TU) 2246-475-05761784-2004 rev. 1-3;Low fire hazard plastic compound, with no smoke and gas emission 20;Polyvinyl chloride non-flammable plastic compound type NGP 30-32;Technical Specifications (TU) 6-01-1328-86 rev. 1-5;Non-flammable plastic compound 21;Polybutylene terephthalate: “Celanex 2001”, “Crastin”, “Ultadur B6550 LN”, etc.;Data sheets and quality certificates of manufacturers;Polybutylene terephthalate designed for the optical module manufacturing 22;Polyester lacing tape;Data sheets and quality certificates of manufacturers;Linear fiber density — 1670 dtex, the fiber should be wound on the bushings with the dimensions: inner rim diameter — 120mm, maximum diameter of the wound fibers — 250 mm. Bushing length — 210 mm 23;Imported hydrophobic fillers for optic fiber;Data sheets and quality certificates of manufacturers;For intra and inter-modular filling of optical cables 24;Laminated steel tape;Data sheets and quality certificates of manufacturers;Steel tape total thickness — 0.250 mm, steel thickness — 0.150 mm, polymer layer thickness on both sides of the tape — 0.050 mm. Elongation at rupture — 15% min. Tape width — 16-34 mm. Inner bushing size — 407 mm, maximum diameter of the wound tape — 1100 mm 25;Technical aramid fiber;Data sheets and quality certificates of manufacturers;Linear fiber density — 1610 dtex, 2420 dtex, 3220 dtex, 8050 dtex and more. The thread should be wound on the bushings: inner bushing diameter — 94 mm, maximum diameter of the wound tape — 220 mm, bushing length — 210 mm 26;Fiberglass threads;Data sheets and quality certificates of manufacturers;Linear thread density — 600 dtex, 1200 dtex. The thread should be wound on the bushings: inner bushing diameter — 94 mm, maximum diameter of the wound tape — 220 mm, bushing length — 210 mm 27;Halogen-free compound LZ0H for mini-module and fiber buffer coating;Data sheets and quality certificates of manufacturers;It should be used for manufacturing of mini-modules and dense buffer coating. Oxygen index — 35% min Material for manufacturing of cable for group laying 28;Halogen-free compound LZ0H for outer sheath;Data sheets and quality certificates of manufacturers;Should be used for laying the sheath on the cable. Oxygen index — 40% min. Material for manufacturing of cable for group laying indoors 29;Steel wire rope;GOST (State Standard) 3062-80;The wire rope should be galvanized, straightened. Wire rope diameter — 1.6-4.0 mm, the wire rope should be set on the drums